摘要:
粉煤灰是煤燃烧后产生的主要固体废弃物,大量堆积危害严重。从粉煤灰中提取氧化铝能同时解决我国面临的铝资源短缺以及粉煤灰堆积问题。从酸法、碱法、酸碱联合法三个方向综述了当前提取氧化铝的工艺,分析了各种方法的长处与不足,并展望了从粉煤灰中提取氧化铝的前景。
Abstract:Fly ash is a main solid waste produced by coal combustion. The large number of accumulation hazards are serious. The extraction of alumina from fly ash can solve the shortage of aluminum fly ash and the accumulation of fly ash in China at the same time. In this paper, some popular processes of extracting alumina from fly ash are reviewed from three general directions: acid method, alkali method and acid-base combination method. The advantages and disadvantages of various methods were analyzed. The prospect of extracting alumina from fly ash was prospected.
-
Key words:
- fly ash /
- alumina /
- acid method /
- alkali method /
- acid-base combination method
-
图 1 硫酸酸溶法流程[19]
Figure 1.
图 2 一步酸溶法[27]
Figure 2.
图 3 预脱硅—碱石灰烧结法工艺[42]
Figure 3.
表 1 我国粉煤灰主要成分平均值
Table 1. Average of main components of fly ash in China
/% SiO2 Al2O3 TiO2 TFeO CaO MgO K2O Na2O MnO P2O5 SO3 LOI 49.22 27.80 1.29 6.63 3.22 0.84 1.21 0.45 0.06 0.28 0.71 7.99 -
[1] 中华人民共和国国家统计局. 中国能源统计年鉴2018[M]. 北京: 中国统计出版社, 2019.
[2] 张静. 粉煤灰综合利用研究进展[J]. 河南化工, 2019(2): 12-17. https://www.cnki.com.cn/Article/CJFDTOTAL-HNHU201902003.htm
[3] 杨星, 呼文奎, 贾飞云, 等. 粉煤灰的综合利用技术研究进展[J]. 能源与环境, 2018(4): 55-57. doi: 10.3969/j.issn.1672-9064.2018.04.025
[4] 侯芹芹, 张创, 赵亚娟, 等. 粉煤灰综合利用研究进展[J]. 应用化工, 2018(6): 1281-1284. doi: 10.3969/j.issn.1671-3206.2018.06.049
[5] 于维河, 孙汉军, 张玉敏. 粉煤灰的环境污染及防治对策[J]. 黑龙江环境通报, 2004(2): 28-29. https://www.cnki.com.cn/Article/CJFDTOTAL-HLJO200402014.htm
[6] 高赛生态, 张永锋, 王敏建. 粉煤灰综合利用现状分析及对策[J]. 内蒙古科技与经济, 2016(18): 87-88. doi: 10.3969/j.issn.1007-6921.2016.18.040
[7] 任启欣, 赵亮, 李超. 粉煤灰对环境的危害及其在建材中的应用[J]. 能源与节能, 2015(10): 113-115. doi: 10.3969/j.issn.2095-0802.2015.10.054
[8] 王爱爱. 高铝粉煤灰提取氧化铝技术的研究现状[J]. 当代化工研究, 2019(2): 131-133. doi: 10.3969/j.issn.1672-8114.2019.02.082
[9] 陈财来, 李进. 粉煤灰提取氧化铝工艺对比及成本分析[J]. 中国氯碱, 2019(12): 37-39. https://www.cnki.com.cn/Article/CJFDTOTAL-JLGZ201912018.htm
[10] 吴玉胜, 张丽丽, 王宏涛, 等. 利用粉煤灰制备高纯氧化铝新技术[J]. 中国材料进展, 2017(3): 195-199. https://www.cnki.com.cn/Article/CJFDTOTAL-XJKB201703008.htm
[11] 许德华. 高铝粉煤灰NH4HSO4/H2SO4法提取氧化铝基础研究[D]. 北京: 中国科学院大学(中国科学院过程工程研究所), 2017.
[12] 袁春林, 张金明, 段玖祥, 等. 我国火电厂粉煤灰的化学成分特征[J]. 电力环境保护, 1998(1): 9-14. https://www.cnki.com.cn/Article/CJFDTOTAL-DLHB199801002.htm
[13] 王宏宾. 粉煤灰提取氧化铝工艺技术研究现状[J]. 化工管理, 2020(12): 189-190. doi: 10.3969/j.issn.1008-4800.2020.12.121
[14] 石振武. 酸浸法提取粉煤灰中氧化铝的研究新进展[J]. 广东化工, 2013(5): 62-63. doi: 10.3969/j.issn.1007-1865.2013.05.032
[15] 李来时, 翟玉春, 吴艳, 等. 硫酸浸取法提取粉煤灰中氧化铝[J]. 轻金属, 2006(12): 9-12. doi: 10.3969/j.issn.1002-1752.2006.12.003
[16] 范艳青, 蒋训雄, 汪胜东, 等. 粉煤灰硫酸化焙烧提取氧化铝的研究[J]. 铜业工程, 2010(2): 34-38. doi: 10.3969/j.issn.1009-3842.2010.02.009
[17] YAO Z T, XIA M S, PRABIRKUMAR S, et al. A review of the alumina recovery from coal fly ash, with a focus in China[J]. Fuel, 2014, 120(15): 74-85. http://www.sciencedirect.com/science/article/pii/S001623611301140X
[18] WU C Y, YU H F, ZHANG H F. Extraction of aluminum by pressure acid-leaching method from coal fly ash[J]. Transactions of Nonferrous Metals Society of China, 2012, 22(9): 2282-2288. doi: 10.1016/S1003-6326(11)61461-1
[19] 许立军, 王永旺, 陈东, 等. 粉煤灰酸法提取氧化铝工艺综述[J]. 无机盐工业, 2019(4): 10-13. https://www.cnki.com.cn/Article/CJFDTOTAL-WJYG201904003.htm
[20] 孙雅珍. 用粉煤灰作原料制备硫酸铝[J]. 粉煤灰综合利用, 2003(2): 46-46. https://www.cnki.com.cn/Article/CJFDTOTAL-FMLE200302018.htm
[21] 高桂梅. 粉煤灰中氧化铝硫酸直接浸取工艺优化[J]. 矿产综合利用, 2019(6): 110-116. https://www.cnki.com.cn/Article/CJFDTOTAL-KCZL201906024.htm
[22] SHI Y, JIANG K X, ZHANG T G. A cleaner electrolysis process to recover alumina from synthetic sulfuric acid leachate of coal fly ash[J]. Hydrometallurgy, 2020, 191: 105196. http://www.sciencedirect.com/science/article/pii/S0304386X19306061
[23] SHI Y, JIANG K X, ZHANG T G, et al. Cleaner alumina production from coal fly ash: Membrane electrolysis designed for sulfuric acid leachate[J]. Journal of Cleaner Production, 2020, 243: 118470. http://www.sciencedirect.com/science/article/pii/S0959652619333402
[24] SHI Y, JIANG K X, ZHANG T G. Cleaner extraction of alumina from coal fly ash: Baking-electrolysis method[J]. Fuel, 2020, 273: 117697. http://www.sciencedirect.com/science/article/pii/S001623612030692X
[25] 魏存弟, 杨殿范, 张东丽, 等. 循环流化床粉煤灰制备结晶氯化铝的方法: CN101054192[P]. 2007-10-17.
[26] 丁亚茹, 张顺. 盐酸溶出-萃取法粉煤灰提取氧化铝[J]. 内蒙古科技与经济, 2017(6): 81-82. https://www.cnki.com.cn/Article/CJFDTOTAL-NMKJ201706044.htm
[27] 郭昭华. 粉煤灰"一步酸溶法"提取氧化铝工艺技术及工业化发展研究[J]. 煤炭工程, 2015(7): 5-8. https://www.cnki.com.cn/Article/CJFDTOTAL-MKSJ201507003.htm
[28] WANG R C, ZHAI Y C, NING Z Q, et al. Thermodynamics and kinetics of alumina extraction from fly ash using an ammonium hydrogen sulfate roasting method[J]. International Journal of Minerals Metallurgy and Materials, 2014, 21(2): 144-149. http://d.wanfangdata.com.cn/Periodical/bjkjdxxb-e201402006
[29] WANG R C, ZHAI Y C, NING Z Q, et al. Kinetics of SiO2 leaching from Al2O3 extracted slag of fly ash with sodium hydroxide solution[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(6): 1928-1936. http://www.sciencedirect.com/science/article/pii/S1003632614632738
[30] 冯亮. 一种提取氧化铝的方法: CN103693666A[P]. 2014-04-02.
[31] 李来时, 吴玉胜. 硫酸氢铵溶液法处理粉煤灰生产冶金级氧化铝工业化可行性分析[J]. 轻金属, 2015(10): 10-13. https://www.cnki.com.cn/Article/CJFDTOTAL-QJSS201510005.htm
[32] 韩战刚. 硫酸氢铵浸出粉煤灰过程氧化铝溶解动力学[D]. 沈阳: 沈阳工业大学, 2016.
[33] 隋丽丽, 翟玉春, 孙莹莹. 粉煤灰硫酸氢铵焙烧法提取氧化铝的研究[J]. 有色金属: 冶炼部分, 2017(4): 20-24. https://www.cnki.com.cn/Article/CJFDTOTAL-METE201704006.htm
[34] 葛欣, 隋丽丽, 尚志航, 等. 硫酸氢铵焙烧粉煤灰混合焙烧反应动力学研究[J]. 轻金属, 2017(3): 14-17. https://www.cnki.com.cn/Article/CJFDTOTAL-QJSS201703009.htm
[35] 陆胜, 方荣利, 赵红. 用石灰烧结自粉化法从粉煤灰中回收高纯超细氧化铝粉的研究[J]. 粉煤灰, 2003(1): 15-17. https://www.cnki.com.cn/Article/CJFDTOTAL-FMHZ200301005.htm
[36] 赵宏, 陆胜, 解晓斌. 用粉煤灰制备高纯超细氧化铝粉的研究[J]. 粉煤灰综合利用, 2002(6): 8-10. https://www.cnki.com.cn/Article/CJFDTOTAL-FMLE200206002.htm
[37] 佚名. 国内首条石灰石烧结法粉煤灰提取氧化铝生产线投产[J]. 铝加工, 2014(6): 18-18. https://www.cnki.com.cn/Article/CJFDTOTAL-LJGO201406010.htm
[38] 许立军, 王永旺, 陈东, 等. 粉煤灰碱法提取氧化铝工艺分析比较[J]. 轻金属, 2018(7): 10-13. https://www.cnki.com.cn/Article/CJFDTOTAL-QJSS201807004.htm
[39] 季惠明, 卢会湘, 郝晓光, 等. 用煅烧-沥滤工艺从粉煤灰中提取高纯超细氧化铝(英文)[J]. 硅酸盐学报, 2007(12): 1657-1660. https://www.cnki.com.cn/Article/CJFDTOTAL-GXYB200712020.htm
[40] 刘能生, 彭金辉, 张利波, 等. 高铝粉煤灰硫酸铵与碳酸钠焙烧活化对比研究[J]. 昆明理工大学学报: 自然科学版, 2016(1): 1-6.
[41] 宋说讲, 孔德顺. 高铝粉煤灰脱硅反应的研究[J]. 化工技术与开发, 2013(6): 3-5. https://www.cnki.com.cn/Article/CJFDTOTAL-GXHG201306003.htm
[42] 肖永丰. 粉煤灰提取氧化铝方法研究[J]. 矿产综合利用, 2020(4): 156-162. https://www.cnki.com.cn/Article/CJFDTOTAL-KCZL202004027.htm
[43] 刘晓婷, 王宝冬, 肖永丰, 等. 高铝粉煤灰碱溶预脱硅过程研究[J]. 中国粉体技术, 2013(6): 24-27. https://www.cnki.com.cn/Article/CJFDTOTAL-FTJS201306007.htm
[44] 肖永丰, 张中华, 赵利军, 等. 煤灰提取氧化铝及中间产物的利用和产品开发[C]//中国环境科学学会. 2016中国环境科学学会学术年会论文集(第三卷). 北京: 中国环境科学学会, 2016: 5.
[45] 陈颖敏, 赵毅, 张建民, 等. 中温法从粉煤灰中回收铝和硅的研究[J]. 电力情报, 1995(3): 35-38. https://www.cnki.com.cn/Article/CJFDTOTAL-DLQB503.011.htm
[46] 苏双青, 马鸿文, 邹丹. 高铝粉煤灰两步碱溶法提取氢氧化铝的试验研究[J]. 矿物学报, 2010(S1): 176-176. https://www.cnki.com.cn/Article/CJFDTOTAL-KWXB2010S1100.htm
[47] 刘中凯, 马淑花, 郑诗礼, 等. 亚熔盐法粉煤灰脱铝渣水热处理后碱含量的影响因素[J]. 过程工程学报, 2014(6): 947-954. https://www.cnki.com.cn/Article/CJFDTOTAL-HGYJ201406008.htm
[48] 黄前, 邹丽霞, 兰鹏, 等. 碳酸钠焙烧粉煤灰提铝研究[J]. 中国煤炭, 2019(10): 70-74. https://www.cnki.com.cn/Article/CJFDTOTAL-ZGME201910017.htm
[49] 祁光霞, 梁振凯, 雷雪飞, 等. 预脱硅-Na2CO3焙烧-酸浸工艺提取粉煤灰中的氧化铝[J]. 高校化学工程学报, 2016(3): 673-679. https://www.cnki.com.cn/Article/CJFDTOTAL-GXHX201603024.htm
[50] TRIPATHY AK, BEHERA B, AISHVARYA V, et al. Sodium fluoride assisted acid leaching of coal fly ash for the extraction of alumina[J]. Minerals Engineering, 2019, 131: 140-145. http://www.sciencedirect.com/science/article/pii/S0892687518304709
[51] GUO C B, ZOU J J, MA S H, et al. Alumina extraction from coal fly ash via low-temperature potassium bisulfate calcination[J]. Minerals, 2019, 9(10): 585. http://www.researchgate.net/publication/336111435_Alumina_Extraction_from_Coal_Fly_Ash_via_Low-Temperature_Potassium_Bisulfate_Calcination
[52] GUO C B, LU Z, YANG J L, et al. A novel perspective process for alumina extraction from coal fly ash via potassium pyrosulfate calcination activation method[J]. Journal of Cleaner Production, 2020, 271: 122703. http://www.sciencedirect.com/science/article/pii/S0959652620327505