Effect of Sodium Hexametaphosphate on Preparation of Ultrafine Gypsum Powder and Its Mechanism
-
摘要:
采用胶体磨以六偏磷酸钠为助磨剂制备超细生石膏粉体，通过激光粒度仪和XRD等方法对超细磨产品进行表征。结果表明，当生石膏料浆质量浓度为20%、排矿口宽度为12 mm、超细磨时间为15 min、六偏磷酸钠用量为0.20%时，可制备出d50为11.12 μm的超细生石膏粉体。六偏磷酸钠的加入引起生石膏颗粒晶粒尺寸与显微应变的变化，使晶格受到破坏，导致生石膏超细磨矿产品结晶度减小并且趋于无定形化。同时磷酸氢根离子可吸附在生石膏颗粒表面并使生石膏表面ζ电位由-8.83 mV负移至-13.39 mV，生石膏料浆的浊度由13 NTU增大至17 NTU，其黏度则由72.49 mPa·s减小至48.91 mPa·s，促进了生石膏颗粒的分散。在上述因素共同作用下，超细生石膏粉体粒度降低，生石膏的超细磨矿效率提高。研究对超细生石膏粉体的制备和提高超细生石膏粉体质量有一定参考意义。
Abstract:Ultrafine gypsum powder was prepared with sodium hexametaphosphate as a grinding agent by colloid mill, and ultra-fine grinding products were characterized through methods such as laser particle size analysis and XRD. The results showed that when the slurry concentration was 20%, and the discharge width was 12 mm, and the dosage of sodium hexametaphosphate was 0.20%, and the ultrafine grinding time was 15 min, the superfine gypsum powder with d50 of 11.12 μm could be obtained. Moreover, the change of grain size and micro-strain of gypsum particles caused by ultra-fine grinding damage the lattice, resulting in the decrease of crystallinity ultrafine grinding products and the tendency of amorphous. In addition, hydrogen phosphate ions could be adsorbed on the surface of gypsum particles to make the ζ potential of gypsum surface shifted from -8.83 mV to -13.39 mV, and the turbidity of gypsum slurry increased from 13 NTU to 17 NTU while its viscosity decreased from 72.49 mPa·s to 48.91 mPa·s, which promotes the dispersion of gypsum particles. Under the combined action of the above factors, the particle size of superfine gypsum powder was reduced and the superfine grinding efficiency of gypsum was improved. The research has certain reference significance for preparing ultrafine gypsum powder and improving the quality of ultrafine gypsum powder.
-
Key words:
- gypsum /
- sodium hexametaphosphate /
- ultrafine grinding /
- mechanism /
- aid-grinding
-
-
表 1 生石膏原料的化学成分
Table 1. Chemical composition of gypsum
/% CaO SO3 SiO2 MgO Na2O +K2O Fe2O3 结晶水 重金属 31.24 44.78 1.42 1.14 0.21 0.16 19.95 0.001 
下载: 导出CSV
-
[1] 范开明, 于海彬. 浅谈柠檬酸石膏的综合利用[J]. 化学工程师, 2020, 34(6): 69-70+9. https://www.cnki.com.cn/Article/CJFDTOTAL-HXGC202006018.htm
[2] 郭大江, 袁运法, 胡浩然, 等. 脱硫石膏性能研究及其在普通硅酸盐水泥中的应用[J]. 硅酸盐通报, 2010, 29(2): 357-360. https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201002022.htm
[3] 陶文宏, 刘宗明, 张明星, 等. 脱硫石膏-石灰-粉煤灰体系胶凝性及水化机理[J]. 济南大学学报(自然科学版), 2010, 24(3): 233-237. doi: 10.3969/j.issn.1671-3559.2010.03.004
[4] 朱志伟, 何东升, 陈飞, 等. 磷石膏预处理与综合利用研究进展[J]. 矿产保护与利用, 2019, 39(4): 19-25. http://kcbh.cbpt.cnki.net/WKD/WebPublication/paperDigest.aspx?paperID=3ed412be-d770-41ea-ba55-8534c228c014
[5] 张敏. 超细粉体团聚的形成机理及消除方法研究[J]. 中国粉体工业, 2019(1): 23-27. http://www.cnki.com.cn/Article/CJFDTotal-ZGFT201901007.htm
[6] 龚志辉, 李海兰, 王增军. 助磨剂应用现状及发展[J]. 四川冶金, 2019, 41(1): 2-6. doi: 10.3969/j.issn.1001-5108.2019.01.002
[7] 余晓光, 胡家城, 石晴. 钙离子和六偏磷酸钠对矿浆流变性影响研究[J]. 非金属矿, 2020, 43(4): 24-27. https://www.cnki.com.cn/Article/CJFDTOTAL-FJSK202004008.htm
[8] 李育彪, 杨旭, 朱虹嘉, 等. 六偏磷酸钠及硅酸钠对海水浮选黄铜矿的影响机理[J]. 金属矿山, 2020(10): 135-140. https://www.cnki.com.cn/Article/CJFDTOTAL-JSKS202010018.htm
[9] MA M. The Dispersive Effect of Sodium Hexametaphosphate on Kaolinite in Saline Water[J]. Clays & Clay Minerals, 2012, 60(4): 405-410. http://adsabs.harvard.edu/abs/2012CCM....60..405M
[10] 唐林生, 冯作锋, 林强. 六偏磷酸钠对石灰石磨的助磨作用[J]. 矿冶工程, 1999, 19(4): 29-31. https://www.cnki.com.cn/Article/CJFDTOTAL-KYGC199904010.htm
[11] 唐林生, 冯作锋, 林强. 石灰石超细磨助磨剂及其助磨机理[J]. 中国有色金属学报, 2000, 10(1): 131-135. https://www.cnki.com.cn/Article/CJFDTOTAL-ZYXZ200001030.htm
[12] 郭建斌. 六偏磷酸钠、碳酸钠提高硅酸锆超细磨矿效率研究[J]. 非金属矿, 2001, 24(2): 35-36. https://www.cnki.com.cn/Article/CJFDTOTAL-FJSK200102012.htm
[13] 王泽红, 徐昌, 李国峰. 六偏磷酸钠提高鄂西鲕状赤铁矿石磨矿效率研究[J]. 金属矿山, 2013(5): 71-74. https://www.cnki.com.cn/Article/CJFDTOTAL-JSKS201305021.htm
[14] 李茂林, 汪彬, 朱晔, 等. 助磨剂对鄂西高磷鲕状赤铁矿磨矿的影响[J]. 武汉科技大学学报, 2011, 34(2): 93-95. https://www.cnki.com.cn/Article/CJFDTOTAL-YEKJ201102004.htm
[15] 郭铁明, 金硕, 吉瑞芳, 等. Mo粉在球磨过程中的机械力效应[J]. 兰州理工大学学报, 2017, 43(3): 6-9. https://www.cnki.com.cn/Article/CJFDTOTAL-GSGY201703002.htm
[16] 刘文萍, 尹周澜, 丁治英, 等. 六偏磷酸钠对黄铁矿超细粉碎影响的研究[J]. 矿产保护与利用, 2006(6): 13-17. http://kcbh.cbpt.cnki.net/WKD/WebPublication/paperDigest.aspx?paperID=3928427f-605d-4e45-a676-460065ad983c
[17] 左倩. 微细粒赤铁矿分散行为及机理研究[D]. 武汉: 武汉科技大学, 2012.
[18] 夏启斌, 李忠, 邱显扬, 等. 六偏磷酸钠对蛇纹石的分散机理研究[J]. 矿冶工程, 2002, 22(2): 51-54. https://www.cnki.com.cn/Article/CJFDTOTAL-KYGC200202015.htm
-
图(8)
表(1)
计量
- 文章访问数: 806
- PDF下载数: 31
- 施引文献: 0