Study on the Preparation and Morphology of Large Aspect Ratio Calcium Sulfate Whisker
-
摘要:
以天然石膏为原料采用水热法制备半水硫酸钙晶须，SEM观察晶须形貌及分析长径比。考察了外加剂、原料粒度、水热温度、pH值、初始料浆浓度、水热时间对硫酸钙晶须形貌影响。结果表明：外加剂提高了天然石膏在水中的溶解度；原料粒度会影响天然石膏的溶解速率，粒度越小溶液越容易达到过饱和状态；水热温度在 < 100 ℃时较难生成硫酸钙晶须；溶液pH值可改变溶液离子质量分数，随着pH值升高晶须平均直径逐渐减小，同时会导致外加剂失效；料浆浓度越高，晶须生长空间越小，溶液体系离子迁移速度降低。在原料粒度4 μm、料浆浓度5%、CuCl2 1.5%（相对于天然石膏质量）、水热温度120 ℃、pH=5.3、水热时间140 min的条件下，制备出平均直径1~2 μm、长径比达160的半水硫酸钙晶须。
Abstract:Natural gypsum was used as raw material in airtight reactor to prepare hemihydrate calcium sulfate whiskers by hydrothermal method, and SEM was utilized to observe the morphology and aspect ratio. The additive, particle size, hydrothermal temperature, pH, initial slurry concentration and hydrothermal time on the morphology of calcium sulfate whisker were investigated. The results showed that additive increased the solubility of natural gypsum in solution; particle size of raw material affected the dissolution rate of natural gypsum, smaller particles easily reached the supersaturated sate; it's difficult to turn into calcium sulfate whisker when hydrothermal temperature was less than 100 ℃; pH of solution can change the mass fraction of ion, and as pH increased the average diameter of whisker gradually decreased, along with being invalid of the additive of CuCl2; the higher slurry concentration was, the smaller the space of whisker growth was and the slower ion transport rate was. The optimum conditions for the preparation were as follows: the diameter of raw material was 4 μm with the slurry concentration at 5%, the content of copper chloride was 1.5%, temperature was 120 ℃, pH=5.3, and reaction time was 140 minutes. Then, the calcium sulfate whisker of average diameter 1~2 μm, aspect ratio 160 were obtained.
-
Key words:
- natural gypsum /
- hydrothermal /
- calcium sulfate whisker
-
-
表 1 天然石膏化学组分及含量
Table 1. Chemical composition and content of natural gypsum
成分 CaO SO3 MgO 含量/% 32.73 46.77 0.091 
下载: 导出CSV
-
[1] 崔益顺.天然石膏粉制备硫酸钙晶须的工艺研究[J].化工矿物与加工, 2017(3):13-16. http://www.cqvip.com/QK/91543X/201001/32840228.html
[2] Wang X, Jin B, Yang L, et al. Effect of CuCl2 on hydrothermal crystallization of calcium sulfate whiskers prepared from FGD gypsum[J]. Crystal Research & Technology, 2015, 50(8):633-640. https://www.researchgate.net/profile/Xiao_Wang139
[3] 邱杨率, 李珺玮, 吕钢, 等.电石渣水热合成石膏晶须[J].中国非金属矿工业导刊, 2008(4):30-32. http://d.wanfangdata.com.cn/Periodical_fjsk200806007.aspx
[4] Zhu Z, Xu L, Chen G, et al. Optimization on tribological properties of aramid fibre and CaSO4, whisker reinforced non-metallic friction material with analytic hierarchy process and preference ranking organization method for enrichment evaluations[J]. Materials & Design, 2010, 31(1):551-555. http://www.academia.edu/14914381/Selecting_the_best_statistical_distribution_with_PROMETHEE_and_GAIA
[5] 张连红. 硫酸钙晶须制备及应用研究[D]. 沈阳: 东北大学, 2010.
http://cdmd.cnki.com.cn/Article/CDMD-10145-1013117073.htm [6] 韩跃新.石膏的应用及其深加工研究[J].矿产保护与利用, 1998(1):10-13. http://kcbh.cbpt.cnki.net/WKD/WebPublication/paperDigest.aspx?paperID=c8e6c1f1-7444-4e76-9182-aabea10e77fd
[7] 杨荣华.石膏资源综合利用及技术开发[J].磷肥与复肥, 2008, 23(6):79-81. http://doi.wanfangdata.com.cn/10.3969/j.issn.1007-6220.2013.04.023
[8] 师存杰, 张兴儒, 郭祖鹏, 等.硫酸钙晶须的制备及其应用进展[J].当代化工, 2010, 39(4):436-438. http://kns.cnki.net/KCMS/detail/detail.aspx?filename=syhh201004031&dbname=CJFD&dbcode=CJFQ
[9] Papageorgiou A, Tzouvalas G, Tsimas S. Use of inorganic setting retarders in cement industry[J]. Cement & Concrete Composites, 2005, 27(2):183-189. https://www.sciencedirect.com/science/article/pii/S0958946504000204
[10] 李帅, 王宇斌, 何廷树, 等.硫酸铁对硫酸钙晶须形貌影响研究[J].矿产保护与利用, 2017(2):96-100. http://kcbh.cbpt.cnki.net/WKD/WebPublication/paperDigest.aspx?paperID=1c484b9d-d88a-4d47-9880-ffbc1894bd32
[11] 朱一民, 张勇, 王晓丽.改性硫酸钙晶须/聚丙烯复合材料力学性能研究[J].矿产保护与利用, 2015(3):46-49. http://kcbh.cbpt.cnki.net/WKD/WebPublication/paperDigest.aspx?paperID=1d821b36-b9d6-4ce6-a742-24342ddb63f6
[12] 何花, 董发勤, 何平.混合助晶剂促进大长径比硫酸钙晶须的调控研究[J].人工晶体学报, 2012, 41(6):1679-1685. http://industry.wanfangdata.com.cn/dl/Detail/Periodical?id=Periodical_rgjtxb98201206038
[13] 蒋绍强. 硫酸钙/纤维素晶须对聚丙烯的改性研究[D]. 成都: 西南石油大学, 2015.
http://cdmd.cnki.com.cn/Article/CDMD-10615-1015599325.htm [14] Miao M, Feng X, Wang G, et al. Direct transformation of FGD gypsum to calcium sulfate hemihydrate whiskers: Preparation, simulations, and process analysis[J]. Particuology, 2015, 19(2):53-59. http://mall.cnki.net/magazine/Article/JCSP201502007.htm
[15] 杨荣华, 吴秀勇, 冯晓宁.用天然石膏制备硫酸钙晶须的研究[J].无机盐工业, 2010, 42(1):44-47. http://xb.suse.edu.cn/upload/20131015/201310150454263159.pdf
[16] 秦军, 谢占金, 于杰, 等.磷石膏制备硫酸钙晶须的初步研究[J].无机盐工业, 2010, 42(10):50-53. doi: 10.3969/j.issn.1006-4990.2010.10.017
[17] 方羊, 窦焰, 孙祥斌, 等.Al3+对水热法制备α-CaSO4·0.5H2O晶须的影响[J].高校化学工程学报, 2017, 31(2):413-419. http://kns.cnki.net/KCMS/detail/detail.aspx?filename=gxhx201702032&dbname=CJFD&dbcode=CJFQ
[18] 王力, 马继红, 郭增维, 等.水热法制备硫酸钙晶须及其结晶形态的研究[J].材料科学与工艺, 2006, 14(6):626-629. http://www.cqvip.com/QK/91902A/200606/23537101.html
[19] Hamdona S K, Hadad U A A. Crystallization of calcium sulfate dihydrate in the presence of some metal ions[J]. Journal of Crystal Growth, 2007, 299(1):146-151. doi: 10.1016/j.jcrysgro.2006.11.139
[20] Azimi G, Papangelakis V G. Thermodynamic modeling and experimental measurement of calcium sulfate in complex aqueous solutions[J]. Fluid Phase Equilibria, 2010, 290(1):88-94. https://www.sciencedirect.com/science/article/pii/S0378381209003902
[21] 袁致涛, 王晓丽, 韩跃新, 等.水热法合成超细硫酸钙晶须[J].东北大学学报(自然科学版), 2008, 29(4):573-576. http://industry.wanfangdata.com.cn/dl/Detail/Periodical?id=Periodical_dbdxxb200804030
-
图(15)
表(1)
计量
- 文章访问数: 561
- PDF下载数: 8
- 施引文献: 0